Ti-Powder

Grade 4 Titanium and Titanium alloy for dentures manufacturing in a laser melting process.

Starbond Ti4 Powder 45

Starbond Ti4 Powder 45

Grade 4-titanium powder for dentures manufacturing in a laser melting process. Starbond Ti4 Powder 45 is biocompatible, with high strength properties and a wide range of indications. Perfectly suitable for the production of bars, crowns, bridges and partial dentures.

  • Grain size: +10/-45µm
  • Compliant with DIN EN ISO 5832-2 and ASTM F67
  • Suitable for processing in the systems:
    SLM125* - further systems on request

Composition in percent by mass:

Ti 99%
N,C,H,Fe,O <1%

Technical properties**:

Proof stress (Rp 0.2) 520MPa
Ultimate tensile strength 590MPa
Elongation 25%
Elastic modulus 110GPa
Vickers hardness >200 HV 5/30
Density 4.5g/cm³
Melting range 1605-1660°C
CTE (25-500°C) 10.1 x 10⁻⁶K⁻¹
CTE (25-600°C) 10.3 x 10⁻⁶K⁻¹
Laser weldable Yes
Type (DIN EN ISO 22674) 4

Trade unit:

2.5kg Ref. 135715

**SLM 125 is a registered trademark of Realizer GmbH
** Standard values; dependent on specific machine settings. Determined after thermal treatment, 700°C with 2h holding time.
Starbond Ti5 Powder 45

Starbond Ti5 Powder 45

Light metal alloy with high corrosion resistance. A very high strength and at the same time low weight distinguishes this alloy.

  • Grain size: +10/-45µm
  • Compliant with EN ISO 5832-3, ASTM F136 and ASTM F3001
  • Suitable for processing in the systems:
    SLM125* - further Systems on request

Composition in percent by mass:

Ti 89%
Al 6%
V 4%
N,C,H,Fe,O <1%

Technical properties**:

Proof stress (Rp 0.2) 920-1150MPa
Ultimate tensile strength 1100-1300MPa
Elongation 3-10%
Elastic modulus 110-120GPa
Vickers hardness 320-380HV 5/30
Density 4,5g/cm³
Melting range 1600°C
CTE (25-600°C) 9 x 10⁻⁶K⁻¹
Laser weldable Yes
Type (DIN EN ISO 22674) 4

Trade unit:

2,5kg Ref. 136715

*SLM 125 is a registered trademark of Realizer GmbH
** Standard values; dependent on specific machine settings. Determined after thermal treatment.